Next Article in Journal
Experimental Evaluation for the Impacts of Conservation Agriculture with Drip Irrigation on Crop Coefficient and Soil Properties in the Sub-Humid Ethiopian Highlands
Previous Article in Journal
The Effect of Human Impact on the Water Quality and Biocoenoses of the Soft Water Lake with Isoetids: Lake Jeleń, NW Poland
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

The Recovery of Phosphorus from Acidic Ultra-High Phosphorous Wastewater by the Struvite Crystallization

1
School of Management, Northwestern Polytechnical University, 127 West Youxi Road, Xian 710072, China
2
Shangtex Architectural Design Research Institute Co., Ltd., Shanghai 200060, China
3
Research Center of Resource Recycling Science and Engineering, School of Environmental and Materials Engineering, Shanghai Polytechnic University, Shanghai 201209, China
*
Authors to whom correspondence should be addressed.
These authors contribute equally to this work.
Water 2020, 12(4), 946; https://doi.org/10.3390/w12040946
Submission received: 4 February 2020 / Revised: 11 March 2020 / Accepted: 18 March 2020 / Published: 26 March 2020
(This article belongs to the Section Wastewater Treatment and Reuse)

Abstract

:
Phosphorus recovery from industrial wastewater has attracted considerable interest. In this study, struvite crystallization method has been used for treatment of high phosphorus wastewater. The new combination agents of Mg5(CO3)4(OH)2·4H2O and NH4Cl were used as the precipitant. The effects of initial pH, n(Mg):n(P), n(N):n(P), and reaction time on the removal of total phosphorus (TP) in wastewater were investigated. The results showed that under the condition of initial pH = 4, Mg:N:P = 1.2:1.1:1, reaction time for 30 min, and static storage for 20 min, the residual amount of TP in wastewater was 2.98 mg /L, and the removal rate of TP reached 99.99%. The mass fraction of P2O5 in the generated sediment reached 25.22%, equivalent to high grade phosphate ore and slow-release fertilizer, so as to realize the recycling and utilization of phosphorus in ultra-high phosphorous wastewater. This work will have practical application potential in treatment of high phosphorus wastewater and environmental management.

1. Introduction

Nowadays, with the increasing demand for aluminum and its alloys in the world, the surface treatment processes, such as phosphating, are often used to protect the surface of materials from oxidation and corrosion [1,2]. The phosphating process contains a series of chemical reactions, and thus lots of acidic ultra-high phosphorous wastewater was produced [3]. The composition of phosphating wastewater produced in the processing of aluminum profiles is complex, and direct discharge will seriously pollute the surrounding ecological environment [4]. When the total phosphorus (TP) concentration in the water body is higher than 0.02 mg/L, it is considered as eutrophic water, which would cause strong algae metabolism, consume a large amount of dissolved oxygen, cause a large number of aquatic organisms to die, and release a large amount of toxic gases: H2S, NH3, CH4, etc., leading to deterioration of water quality, disrupting the ecological balance and stability of water bodies, and increasing the difficulty and cost of water treatment [5]. So, the removal of phosphorus from wastewater is of great significance for environmental protection.
Current methods for phosphorus removal include biological method, physical adsorption method, electrodialysis method, ion exchange method, chemical precipitation method, etc., [6]. The biological method is susceptible to factors such as wastewater chemical composition, process parameters, and structure size [7]. Therefore, the process of biological method is unstable, and the phosphorus removal in the form of sludge will eventually cause secondary pollution [8]. The physical adsorption has a disadvantage of low adsorption efficiency of the adsorbent [9]. The electrodialysis process has high requirements on the ion selectivity of the permeation membrane itself, and is only suitable for enterprises with a small amount of wastewater with a single component [10]. Ion exchange method also has high selectivity for exchange objects, and can only handle solutions with lower ion concentrations [11]. The reproducibility of ion exchange resins is also a major problem. The chemical precipitation treatment of phosphorus is to separate the phosphorus by the precipitation reaction between orthophosphate and metal ions. Common metal salts that can react with soluble phosphate to form insoluble matter include calcium, aluminum, ammonium, magnesium salts, and iron [12]. The chemical precipitation method has a high removal rate and is widely used in the treatment of industrial high-concentration phosphorus-containing wastewater, but this method can only “remove phosphorus,” not “recycle phosphorus” [13]. Phosphorus is a precious natural resource on the earth, and it is also one of the indispensable elements that make up living matter. The large-scale exploitation of phosphate rock and the neglect of phosphorus resource recovery have led to the depletion of phosphorus resources [14]. Because of the non-renewable nature of phosphorus resources, the sustainable use of phosphorus resources has received increasing attention in recent years [15]. Research on recovering phosphorus using struvite (MgNH4PO4·6H2O, referred to as MAP) crystallization has also received widespread attention from scientists [16]. Struvite crystallization means that when the concentrations of Mg2+, PO43−, and NH4+ in wastewater reaches the solubility product (Ksp) of struvite, NH4+ and PO43− are precipitated and removed as struvite crystals, as shown in formula (1).
Mg2++NH4++HnPO43−n+6H2O → MgNH4PO4·6H2O↓ + nH+
This method can not only efficiently remove high-concentration ammonia nitrogen and water-soluble phosphorus in wastewater, but also produce struvite as a slow-release fertilizer for agricultural production and flower cultivation [17]. Struvite crystallization has been extensively studied for removal of nitrogen and phosphorus in wastewater [17,18]. However, for high-concentration acidic phosphorus-containing wastewater (total phosphorus content of ~24,500 mg/L) generated in the processing of aluminum profiles, reducing the phosphorus content to the discharge standard (≤5 mg/L) remains a challenge. Thus, the main aim of this work is studying the factors affecting the recovery of phosphorus in acidic ultrahigh-phosphorus wastewater by struvite crystallization, such as the proportion of reactant materials, initial pH, and reaction time. The study found that using basic magnesium carbonate as the source of magnesium for struvite precipitation can take advantage of the alkaline nature of the basic magnesium carbonate aqueous solution, raise the pH of wastewater, and reduce the use of alkali. It can also ensure that the TP content in the treated wastewater meets the standard discharge and recover higher purity phosphorus resources, which has a high potential economic value.

2. Materials and Methods

2.1. Materials

Calcium oxide was purchased from Tianjin Bodi Chemical Co., Ltd., and magnesium chloride was purchased from Kunming Huangbao Trading Company. Ammonium chloride, calcium chloride, sulfuric acid, magnesium hydroxide, potassium antimony tartrate, nitric acid, and perchloric acid were purchased from Sinopharm Chemical Reagent Co., Ltd. (Shanghai, China). Ammonium molybdate was purchased from Tianjin Chemical Reagent Kaida Plant, and ascorbic acid was purchased from Tianjin Dingshengxin Chemical Co., Ltd.; sodium hydroxide was purchased from Shanghai Titan Technology Co., Ltd. Ammonium bicarbonate was purchased from Shanghai Aladdin Biochemical Technology Co., Ltd. The filter paper (Φ15, medium speed) was purchased from Wendong Chemical Co., Ltd. (Shanghai, China), and the needle filter (0.22 μm) was purchased from ALWSCI (Hangzhou, China). All reagents were of analytical purity and not further processed before use.

2.2. Methods

The wastewater in the experiment is provided by Haiyan County Saixin Metal Surface Treatment Co., Ltd. (Haiyan, China), with the main pollutants in wastewater is shown in Table 1. It was determined that the proportion of phosphorus in soluble orthophosphate to TP was 98.52%. In order to eliminate the influence of sulfate ion in the waste liquid and recover the high-purity phosphorus resources, the waste liquid needs to be pre-treated as follows: an appropriate amount of the above-mentioned wastewater was taken, and calcium oxide was added thereto at a concentration of 38 g/L to remove sulfate. The filter was used to filter out the precipitate. After analysis, it was found that the amount of dry mud produced in this step was about 73 g/L, and the main component was calcium sulfate. The removal rate of sulfate in the waste liquid reached 90%, while the concentration of phosphate was basically unchanged, and the pH of the solution increased from 0.6 to 1.8. Continuously adding sodium hydroxide to the filtered waste liquid to a pH of 4.0, a precipitate is formed due to the presence of small amount aluminum ions in the wastewater. The supernatant was filtered and the magnesium salt and ammonium salt were added according to the set molar ratio. Struvite precipitated in the waste liquid after stirring for 30 minutes, and then it was allowed to stand for 20 minutes. After that, the supernatant was filtered and the TP content was measured.

2.3. Analysis

The precipitate was dried at 75 °C to constant weight and ground to a powder to analyze the crystal composition and microstructure by X-ray diffraction (XRD, Rigaku-D/max 2550 PC, Japan) and scanning electron microscope (SEM, Hitachi S-4800, Japan). TP is measured using ammonium molybdate spectrophotometry (Chinese National Standard: GB/T 11894-1989). The model of the spectrophotometer is V1800, Unico Instrument Co., Ltd., Shanghai. The concentration of sulfate ion was measured by ion chromatography (ICS-2100, Dion (China) Co., Ltd.). The concentration of metals ions was measured by inductively coupled plasma atomic emission spectroscopy (ICP-AES, A-6300, Thermo Fisher, USA). The ammonia nitrogen content in the wastewater was measured using the Nessler’s reagent spectrophotometry (China Environmental Industry Standard: HJ 535-2009), and the model of the spectrophotometer was the same as that used to measure the TP content.

3. Results and Discussion

3.1. Effect of Initial pH

The original pH of the experimental wastewater of 0.6 is not suitable for struvite precipitation [19]. If the pH is directly adjusted to be alkaline, the amount of alkaline solution consumed is too large and the cost is too high. The group of reagents of Mg5(CO3)4(OH)2·4H2O and NH4Cl was selected in consideration of the fact that Mg5(CO3)4(OH)2·4H2O can be dissolved in dilute acid and neutralize the acid in solution to a greater extent than the ammonium radical hydrolysis to produce hydrogen. So adjust the pH of the original wastewater to 4.0, 5.0, and 6.0, and take the filtrate after filtration. According to the concentration of TP in the filtrate, add Mg5(CO3)4(OH)2·4H2O and NH4Cl according to the theoretical Mg:N:P molar ratio of 1:1:1. The reaction was stirred for 30 minutes, left to stand for 20 minutes, filtered, the TP content and pH in the filtrate were measured, and the TP removal rate was calculated. The experimental data are shown in Table 2.
As shown in Table 2, Mg5(CO3)4(OH)2·4H2O and NH4Cl were added with Mg:N:P at a molar ratio of 1:1:1. Under different pH conditions, all the TP concentrations were reduced to less than 10 mg/L, and the TP removal rate all reached 99.98%. The pH value of the solution after the reaction is in the range of 7.3–8.2, which belongs to the suitable pH range for struvite crystals. From the data in the table above, it can be seen that the initial pH is suitable between 4 and 6, but it is also necessary to determine the optimal working conditions in combination with the material addition ratio.

3.2. Effects of Mg/P and N/P Molar Ratios on TP Removal

Under the condition of N:P as 1:1, adjust the pH to 4.0, 5.0, and 6.0, respectively, add Mg5(CO3)4(OH)2·4H2O with different Mg: P molar ratio, stir the solution for 30 min and let it stand for 20 min. The effects of Mg:P with different molar ratios on TP removal is shown in Figure 1A. The TP removal in wastewater is improved with increasing of Mg:P molar ratio. Among them, when the initial pH is 4.0, the overall TP removal effect is the best. When Mg:P reached 1.1:1, the TP concentration decreased to less than 5 mg/L. When Mg:P is higher than 1.3:1, the effect of TP removal is basically unchanged or even reduced.
Fixing Mg:P to 1:1, adjusting different pH to 4.0, 5.0, and 6.0, and then NH4Cl with different N:P molar ratio was added into the wastewater. The effect of molar ratios of N: P on TP removal is shown in Figure 1B. It can be seen that when N:P molar ratio is increased, the TP concentrations in the wastewater also decrease. When the initial pH is 6.0, the overall removal effect of TP is the best, followed by the phosphorus removal effect with the initial pH at 4.0. When N:P is 1.2:1, the minimum remaining amount of TP is 3.74 mg/L. When N: P is higher than 1.2:1, the change of TP concentration is small and tends to be stable.

3.3. Determination of the Optimal Molar Ratio of Mg/N/P

Increasing Mg:P and N:P separately can promote the removal of phosphorus in wastewater, so a set of cross-contrast experiments are designed, as shown in Table 2. The experimental conditions are: adjusting the pH to 4.0, stirring the solution 30 min, and letting it to stand for 20 min. The experimental design and results are shown in Table 3.
As shown in Table 3, it can be seen that the combined experimental results are better than the individual experimental results. The remaining amount of TP is stable below 5 mg/L, and the pH of the solution after the reaction changes in a small range between 7.6 and 7.9. The sludge yields listed in Table 3 refer to the mass of the sediment produced in the single process of struvite precipitation after drying. Considering that the increase of NH4Cl dosage will lead to the increase of ammonia nitrogen concentration in the sample, so Mg:N:P = 1.2:1.1:1 is selected as the best dosage ratio, while the TP concentration was 2.98 mg/L.

3.4. Effect of Reaction Time on TP Removal

Adjust the pH = 4.0, control the material dosing ratio of Mg:N:P = 1.2:1.1:1, and leave it for 20 min to observe the effect of TP removal under different stirring reaction times. As can be seen from Figure 2, when the reaction time was 10 minutes, the TP concentration was 3.30 mg/L, and it remained almost unchanged when the reaction time reached 20 minutes. It can be seen that the formation rate of struvite crystals is very fast, as observed during the experiment that a large amount of precipitation will occur immediately after the magnesium salt and the ammonium salt are added. Comprehensive consideration, the reaction time of 30 min was selected as the optimal reaction time. At this time, the TP concentration was reduced to 2.98 mg/L, which meet the discharged sewage standard in China (≤5 mg/L, Quality Standards for Sewage Discharge into Urban Sewers, GB 31962-2015) and can ensure the full progress of the reaction and reduce energy consumption.

3.5. Comparison of Struvite Methods Using Different Combinations of Agents

Comparison of struvite methods using three different combinations of agents are listed in Table 4. The TP removal rate by the agents groups of [Mg(OH)2+NH4Cl], [MgCl2·6H2O+NH4HCO4], and [Mg5(CO3)4(OH)2·4H2O+NH4Cl] are 4.91 mg/L, 5.72 mg/L, and 2.98 mg/L, separately. In the three groups of reagents, the consumption of magnesium hydroxide was less, because of its lower solubility [20]. Magnesium chloride has low toxicity and excessive intake is harmful to human health, so it is not suitable for large-scale use to reduce phosphorus ions [21,22]. In terms of the pH value of the solution after the reaction, the pH values of the three groups all meet the discharged sewage standard in China (range of 6.5–9.5, Quality Standards for Sewage Discharge into Urban Sewers, GB 31962-2015). In addition, it can be found that the concentration of sulfate in the wastewater is also reduced. This is because the sulfate and the magnesium salt also react to form a magnesium sulfate precipitate, which can be confirmed from the XRD patterns of struvite precipitation. It can be seen in Figure 3 that the main component of struvite precipitation is magnesium ammonium phosphate, but there is also a small amount of magnesium sulfate [23].

3.6. SEM Analysis of Struvite Precipitation

As shown in Figure 4, the precipitated powder obtained by the reaction of Mg5(CO3)4(OH)2·4H2O and NH4Cl was magnified 1500 (A) and 8000 (B) times, respectively. As shown in Figure 4A, the struvite precipitation was observed as guano-like clusters. Combined with the experimental phenomena recorded during the experimental process, it was verified that the struvite deposits formed by the reaction are easy to settle in water, which is beneficial to the recycling and actual use. As shown in Figure 4B, the surface of the struvite sediment can be seen as a whole in a layered form, which indicates that the struvite precipitates in a layered manner, and is arranged neatly and regularly. However, it can also be seen that a small amount of irregular substances are mixed in, and the impurities do not have a specific form. According to the ionic data of the reaction process, it is likely that the residual Mg5(CO3)4(OH)2·4H2O is undissolved solid, but the proportion is very small.

3.7. Analysis of Nutrients in Struvite Precipitation

The nutrient element analysis was performed on the precipitate generated under the conditions of initial pH of 4.0, Mg:N:P of 1.2:1.1:1, stirring reaction time of 30 minutes. The specific operation is: accurately weigh 0.50 g of the dried precipitate, dissolve it in dilute hydrochloric acid, and make it to a volume of 100 mL; during measuring, the concentration is diluted according to different measurement ranges of Mg, N, and P. The mass fraction of Mg, N, and P in the precipitate was calculated based on MgO, N, and P2O5 [24]. The results are shown in Table 5:
It can be obtained from Table 5 that the reference mass fractions of Mg, N, and P in the precipitate are close to the theoretical values of the corresponding mass fraction in struvite, which indicates that the main constituent of the precipitate is MAP. According to the classification standards of China’s phosphate rock, phosphate rock has a mass fraction of P2O5 in the range of 20% to 30%, which belongs to Grade II phosphate rock. Compared with natural phosphate rock, there is less toxic and harmful impurities in the struvite precipitation produced in this study, which is easy to purify and separate, and has more economic value [25].

4. Conclusions

In summary, the main aim of this work is studying the factors affecting the recovery of phosphorus in acidic ultrahigh-phosphorus wastewater by struvite crystallization, such as the proportion of reactant materials, initial pH, and reaction time. A feasible TP treatment process is designed to make the TP concentration reach the discharge standard in the experiments. This work innovatively uses basic magnesium carbonate as the magnesium source in the struvite precipitation method, which has a higher solubility than magnesium hydroxide, and is more suitable for treating high-concentration acidic phosphorus-containing wastewater. With the conditions of using reagents of [Mg5(CO3)4(OH)2·4H2O + NH4Cl], initial pH = 4.0, Mg:N:P molar ratio of 1.2:1.1:1, and reaction time of 30 min, the remaining TP concentration was 2.98 mg/L, and the TP removal rate reached 99.99%. XRD pattern analysis confirmed that the main component of struvite sediment was ammonium magnesium phosphate. The nutritional element analysis of the generated struvite precipitated that the mass fraction in P2O5 reached 25.22%, which is equivalent to high-grade phosphate rock, and it is determined that the recovered struvite has high economic value.

Author Contributions

Methodology, Q.L.; validation, S.W. and L.Z.; formal analysis, L.W.; data curation, Q.L.; writing—original draft preparation, Z.S., X.W., and S.W.; writing—review and editing, L.Z.; funding acquisition, L.Z. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by Natural Science Foundation of China (Nos. 21806101, 51476094, 51590901), Natural Science Foundation of Shanghai (Nos. 16ZR1412600, 15ZR1416900), Gaoyuan Discipline of Shanghai-Environmental Science and Engineering (Resource Recycling Science and Engineering), Shanghai Eastern Professorship grant, Shu Guang project supported by Shanghai Municipal Education Commission and Shanghai Education Development Foundation (No. 15SG52).

Acknowledgments

The authors thank Zhongping Xu for his help in SEM characterization.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Tsuji, N.; Ito, Y.; Saito, Y.; Minamino, Y. Strength and ductility of ultrafine grained aluminum and iron produced by ARB and annealing. Scr. Mater. 2002, 47, 893–899. [Google Scholar] [CrossRef]
  2. Lin, B.L.; Lu, J.T.; Kong, G. Synergistic corrosion protection for galvanized steel by phosphating and sodium silicate post-sealing. Surf. Coat. Technol. 2008, 202, 1831–1838. [Google Scholar] [CrossRef]
  3. Akhtar, A.S.; Wong, K.C.; Mitchell, K.A.R. The effect of pH and role of Ni2+ in zinc phosphating of 2024-Al alloy. Part I: Macroscopic studies with XPS and SEM. Appl. Surf. Sci. 2006, 253, 493–501. [Google Scholar] [CrossRef]
  4. Jin, Y.; Qu, R.; Zuo, Z.; Tang, H. Coating Process for Aluminium Alloy Structure of Bus. Paint Coat. Ind. 2016, 46, 61–64. [Google Scholar]
  5. Li, Q.; Gu, P.; Ji, X.; Li, H.; Zhang, J.; Zheng, Z. Response of submerged macrophytes and periphyton biofilm to water flow in eutrophic environment: Plant structural, physicochemical and microbial properties. Ecotoxicol. Environ. Saf. 2020, 189, 109990. [Google Scholar] [CrossRef]
  6. Othman, A.; Dumitrescu, E.; Andreescu, D.; Andreescu, S. Nanoporous Sorbents for the Removal and Recovery of Phosphorus from Eutrophic Waters: Sustainability Challenges and Solutions. ACS Sustain. Chem. Eng. 2018, 6, 12542–12561. [Google Scholar] [CrossRef]
  7. Wang, B.; Zeng, W.; Fan, Z.; Wang, C.; Meng, Q.; Peng, Y. Effects of polyaluminium chloride addition on community structures of polyphosphate and glycogen accumulating organisms in biological phosphorus removal (BPR) systems. Bioresour. Technol. 2020, 297, 122431. [Google Scholar] [CrossRef]
  8. Bertanza, G.; Menoni, L.; Capoferri, G.U.; Pedrazzani, R. Promoting biological phosphorus removal in a full scale pre-denitrification wastewater treatment plant. J. Environ. Manag. 2020, 254, 109803. [Google Scholar] [CrossRef]
  9. Qiang, J.; Zhou, Z.; Wang, K.; Qiu, Z.; Zhi, H.; Yuan, Y.; Zhang, Y.; Jiang, Y.; Zhao, X.; Wang, Z.; et al. Coupling ammonia nitrogen adsorption and regeneration unit with a high-load anoxic/aerobic process to achieve rapid and efficient pollutants removal for wastewater treatment. Water Res. 2020, 170, 115280. [Google Scholar] [CrossRef] [PubMed]
  10. Gally, C.R.; Benvenuti, T.; da Trindade, C.D.M.; Rodrigues, M.A.S.; Zoppas-Ferreira, J.; Perez-Herranz, V.; Bernardes, A.M. Electrodialysis for the tertiary treatment of municipal wastewater: Efficiency of ion removal and ageing of ion exchange membranes. J. Environ. Chem. Eng. 2018, 6, 5855–5869. [Google Scholar] [CrossRef]
  11. Koh, K.Y.; Zhang, S.; Chen, J.P. Hydrothermally synthesized lanthanum carbonate nanorod for adsorption of phosphorus: Material synthesis and optimization, and demonstration of excellent performance. Chem. Eng. J. 2020, 380, 122153. [Google Scholar] [CrossRef]
  12. Hu, L.; Yu, J.; Luo, H.; Wang, H.; Xu, P.; Zhang, Y. Simultaneous recovery of ammonium, potassium and magnesium from produced water by struvite precipitation. Chem. Eng. J. 2020, 382, 123001. [Google Scholar] [CrossRef]
  13. Pinatha, Y.; Polprasert, C.; Englande, A.J., Jr. Product and cost perspectives of phosphorus recovery from human urine using solid waste ash and sea salt addition—A case of Thailand. Sci. Total Environ. 2020, 713, 136514. [Google Scholar] [CrossRef] [PubMed]
  14. Sena, M.; Morris, M.R.; Seib, M.; Hicks, A. An exploration of economic valuation of phosphorus in the environment and its implications in decision making for resource recovery. Water Res. 2019, 172, 115449. [Google Scholar] [CrossRef]
  15. Duan, M.; O’Dwyer, E.; Stuckey, D.C.; Guo, M. Wastewater to Resource: Design of a Sustainable Phosphorus Recovery System. Chemistryopen 2019, 8, 1109–1120. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  16. Law, K.P.; Pagilla, K.R. Reclaimed phosphorus commodity reserve from water resource recovery facilities-A strategic regional concept towards phosphorus recovery. Resour. Conserv. Recycl. 2019, 150, 104429. [Google Scholar] [CrossRef]
  17. Xie, M.; Nghiem, L.D.; Price, W.E.; Elimelech, M. Toward Resource Recovery from Wastewater: Extraction of Phosphorus from Digested Sludge Using a Hybrid Forward Osmosis-Membrane Distillation Process. Environ. Sci. Technol. Lett. 2014, 1, 191–195. [Google Scholar] [CrossRef]
  18. Shimamura, K.; Ishikawa, H.; Mizuoka, A.; Hirasawa, I. Development of a process for the recovery of phosphorus resource from digested sludge by crystallization technology. Water Sci. Technol. 2008, 57, 451–456. [Google Scholar] [CrossRef]
  19. Kekedy-Nagy, L.; Teymouri, A.; Herring, A.M.; Greenlee, L.F. Electrochemical removal and recovery of phosphorus as struvite in an acidic environment using pure magnesium vs. the AZ31 magnesium alloy as the anode. Chem. Eng. J. 2020, 380, 122480. [Google Scholar] [CrossRef]
  20. Babic-Ivancic, V.; Kontrec, J.; Brecevic, L.; Kralj, D. Kinetics of struvite to newberyite transformation in the precipitation system MgCl2-NH4H2PO4-NaOH-H2O. Water Res. 2006, 40, 3447–3455. [Google Scholar] [CrossRef]
  21. Fischer, F.; Bastian, C.; Happe, M.; Mabillard, E.; Schmidt, N. Microbial fuel cell enables phosphate recovery from digested sewage sludge as struvite. Bioresour. Technol. 2011, 102, 5824–5830. [Google Scholar] [CrossRef] [PubMed]
  22. Tanaka, H.; Hagiwara, A.; Kurata, Y.; Ogiso, T.; Futakuchi, M.; Ito, N. Thirteen-week oral toxicity study of magnesium chloride in B6C3F1 mice. Toxicol. Lett. 1994, 73, 25–32. [Google Scholar] [CrossRef]
  23. Agudosi, E.S.; Salleh, M.A.M.; Abdullah, E.C.; Mubarak, N.M.; Khalid, M.; Azni, A.A. Characterization of crystallized struvite on wastewater treatment equipment: Prospects for crystal fertilizer production. Desalin. Water Treat. 2018, 113, 205–212. [Google Scholar] [CrossRef]
  24. Wen, G.; Huang, L.; Zhang, X.; Hu, Z. Uptake of nutrients and heavy metals in struvite recovered from a mixed wastewater of human urine and municipal sewage by two vegetables in calcareous soil. Environ. Technol. Innov. 2019, 15, 100384. [Google Scholar] [CrossRef]
  25. Fan, X.; Rui, Y.; Han, X.; Yang, J.; Wang, Y.; Zhang, Q. Spray-coated monodispersed SnO2 microsphere films as scaffold layers for efficient mesoscopic perovskite solar cells. J. Power Sources 2020, 448, 227405. [Google Scholar] [CrossRef]
Figure 1. Effect of changing Mg:P (A) and N:P (B) on TP removal under different pH conditions.
Figure 1. Effect of changing Mg:P (A) and N:P (B) on TP removal under different pH conditions.
Water 12 00946 g001
Figure 2. Effect of reaction time on TP removal.
Figure 2. Effect of reaction time on TP removal.
Water 12 00946 g002
Figure 3. XRD patterns of struvite precipitation obtained by the reaction of Mg5(CO3)4(OH)2·4H2O and NH4Cl.
Figure 3. XRD patterns of struvite precipitation obtained by the reaction of Mg5(CO3)4(OH)2·4H2O and NH4Cl.
Water 12 00946 g003
Figure 4. SEM diagram of the precipitated powder obtained by the reaction of Mg5(CO3)4(OH)2·4H2O and NH4Cl magnified 1500 (A) and 8000 (B) times.
Figure 4. SEM diagram of the precipitated powder obtained by the reaction of Mg5(CO3)4(OH)2·4H2O and NH4Cl magnified 1500 (A) and 8000 (B) times.
Water 12 00946 g004
Table 1. The parameters of the wastewater sample.
Table 1. The parameters of the wastewater sample.
ItemsUnitsParameters
pH 0.6
TPmg/L24,000–25,000 (avg.: 24,500.00)
Almg/L4300.00
SO4mg/L50,000–60,000 (avg.: 55,000.00)
NO3mg/L302.90
Clmg/L164.50
Momg/L46.30
Timg/L42.10
Femg/L77.60
Asµg/L17.70
Sbµg/L56.90
Table 2. Concentration of total phosphorus (TP) after reaction at different initial pH.
Table 2. Concentration of total phosphorus (TP) after reaction at different initial pH.
Initial pHMg:N:PTP (mg/L)pH After Reaction
4.01:1:15.867.30
5.01:1:16.107.80
6.01:1:15.688.10
Table 3. Combination experiment of different Mg:N:P.
Table 3. Combination experiment of different Mg:N:P.
Mg:N:PTP (mg/L)TP Removal RatepH After ReactionSludge Yield (g/L)
1.1:1.1:13.9499.98%7.743.33
1.15:1.1:13.7099.98%7.843.95
1.2:1.1:12.9899.99%7.844.70
1.1:1.15:13.6699.99%7.743.24
1.15:1.15:12.9499.99%7.745.90
1.2:1.15:12.8699.99%7.748.86
1.1:1.2:13.3099.99%7.643.28
1.15:1.2:12.8699.99%7.746.49
1.2:1.2:12.7899.99%7.746.86
Table 4. Comprehensive comparison of ammonium magnesium combined sedimentation agent.
Table 4. Comprehensive comparison of ammonium magnesium combined sedimentation agent.
ParametersMg(OH)2 + NH4ClMgCl2·6H2O + NH4HCO4Mg5(CO3)4(OH)2·4H2O + NH4Cl
Amount of reagent used (optimal molar ratio in single experiment)CaO g/L38.0038.0038.00
NaOH mg/L14.6028.1014.60
Mg(OH)2 g/L25.87//
NH4Cl g/L14.84/16.30
Mg5(CO3)4(OH)2·4H2O g/L//32.20
MgCl2·6H2O g/L/50.85/
NH4HCO4 g/L/25.69/
Content of residual ionsTP mg/L4.915.722.98
SO42− mg/L5054.004205.004415.00
Amount of precipitationRecycled struvite48.6049.8044.70
CaO pretreatment73.0073.0073.00
Adjust pH35.0041.4035.00
pH after reaction8.67.67.8
Table 5. Composition analysis of struvite precipitation.
Table 5. Composition analysis of struvite precipitation.
Ingredient Contentω(MgO)/%ω(N)/%ω(P2O5)/%
Theoretical value of struvite16.435.7028.92
Actual value of precipitate17.084.0025.22

Share and Cite

MDPI and ACS Style

Li, Q.; Wang, S.; Wang, L.; Zhang, L.; Wan, X.; Sun, Z. The Recovery of Phosphorus from Acidic Ultra-High Phosphorous Wastewater by the Struvite Crystallization. Water 2020, 12, 946. https://doi.org/10.3390/w12040946

AMA Style

Li Q, Wang S, Wang L, Zhang L, Wan X, Sun Z. The Recovery of Phosphorus from Acidic Ultra-High Phosphorous Wastewater by the Struvite Crystallization. Water. 2020; 12(4):946. https://doi.org/10.3390/w12040946

Chicago/Turabian Style

Li, Qiang, Song Wang, Lifang Wang, Li Zhang, Xiaohui Wan, and Zhiguo Sun. 2020. "The Recovery of Phosphorus from Acidic Ultra-High Phosphorous Wastewater by the Struvite Crystallization" Water 12, no. 4: 946. https://doi.org/10.3390/w12040946

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop